SNOEK-KSTER RELAXATION IN Ta-O

用低频扭摆测量了掺氧的超纯Ta的Snoek-Kstcr弛豫.观察到了四种不同类型的S-K弛豫过程.在氧含量较低因而位错具有非饱和的填隙原子气团的条件下出现“SK-1”和“SK-2”弛豫.在氧含量较高的饱和气团条件下出现“SK-4”弛豫,而“SK-5”也属于非饱和气团的条件.本文还观测到随退火温度的提高和氧含量的增加,出现SK-5弛豫的试样有逐渐向sK-4弛豫过渡的趋势.除了SK-1弛豫对退火较不稳定以外,其它弛豫过程均较为稳定.比较了前人的测量结果与本文的实验数据.表明文献报道的Ta的S-K弛豫分别属于本文的不同类型的S-K弛豫.     

THE MIGRATION OF IMPURITY ATOMS AND HYDROGEN EMBRITTLEMENT CRACKING

<正> 一般认为裂纹材料的氢脆开裂是一个和氢原子扩散有关的过程。在负载条件下,氢原子将从四周扩散到裂纹尖端高应力区,当局部浓度达到临界值即起始开裂。开裂的每一步只能跃进一定距离,当裂纹扩展到氢含量很低的区域便暂时停止,然后,氢原子又再扩散聚集,如此往复,裂纹以不连续开裂方式向前扩展。     

OBSERVATION ON SPUTTERING SURFACE OF ALLOYS IN GLOW DISCHARGE

Glow discharge cathodic sputtering of alloys containing second phase precipitates or injectedoxide particles has been observed with energy dispersive X-ray spectrometer and scanningelectron microprobe.It was shown that the formation of cones during the sputtering in thesealloys is due to masking of the matrix by glow sputtering second phase precipitates or oxideparticles.At steady state,the density of cottes were found to be a function of the densities pre-cipitates or oxide particles in bulk alloy.In addition to the changes of local sputtering rate,theelectrostatic effect may play a role on the formation fo cones.     

ON THE COMPOSITION UNIFORMITY AND SHAPE COEFFICIENT OF MOLTEN POOL BY LASER ALLOYING

The effect of the laser processing parameters on the composition uniformity and shapecoefficient of fusion zone with laser surface alloyed Cr plated on medium carbon low alloysteel has been studied.It was found that the composition uniformity depends on the shapecoefficient of fusion zone,and the later is a function of both power density and interactiontime.If the power density is fixed to a certain value,the shape coefficient is directly,propor-tional to the interaction time.A completely,uniform molten pool can be obtained,when theshape coefficient is between 1.6 and 3.0.     

EFFECT OF AGING ON HYDROGEN EMBRITTLEMENT SUSCEPTIBILITY OF STEEL Cr21Ni6Mn9N

Effects of 650℃ aging for 1—1000 h on structure and hydrogen embrittlement susceptibility(HES)of steel Cr21Ni6Mn9N have been investigated.The results show that M_(23)C_6 typecarbide precipitates at grain boundaries and Cr-depletive region appears beside them duringaging.The precipitates grow and connect each other as the aging time prolongs.Meanwhile,the degree of Cr-depletion aggravates first and then recovers gradually while the aging time isvery long,i.e.,1000 h.The HES of the steel increases with increasing aging time but does notreduce with the recovery of Cr content at the Cr-depletive region.That implies that the ex-isting of carbides at grain boundaries might be the main reason which promotes the HES ofsteel during aging.     

AN EXPRESSION OF QUANTITATIVE PHASE ANALYSIS BY X-RAY WITHOUT RELATIVE CALIBRATION STANDARD

在一组能满足Zevin法要求的样品中,如果每个样品有一个含量为已知的相,可以导出X射线无标定量相分析新的表达式.已知含量的相可以是用别的方法测定的样品中的一个相,也可以是把一个已知重量的物相人为地混入样品中的外来物相.在新的表达式中,相的重量分数只与每个样品中各相的衍射强度和已知含量相的衍射强度间比值有关.这与Zevin法有所不同.在新的方法中不要求给出各个样品或者各个相的吸收系数,也不要求各个样品都在全同的实验条件下进行实验.但在Zevin法中,这两个条件都必须完全得到满足.实验证明了新方法的可靠性.     

1Cr18Ni9Ti不锈钢微晶的耐局部腐蚀性能研究

利用磁控离子溅射技术得到bcc结构的1Cr18Ni9Ti不锈钢微晶溅射层,在不同溅射条件下可以得到(110)和(211)两种择优取向的微晶。用电化学方法研究表明,这两种微晶的耐局部腐蚀性能都较正常晶粒有明显提高,且(110)择优取向微晶的耐局部腐蚀性能较(211)择优取向微晶的耐局部腐蚀性能更好。     

细磨活化对白钨矿浸取行为的影响SCIEI

本文研究了细磨活化对白钨矿浸取行为的影响.实验结果表明,细磨活化后白钨矿在HCl-Na_3PO_4介质中的浸出速率显著加快,钨的浸出率由原来的约8％提高到99％以上.红外光谱和X射线分析结果表明,细磨除了使白钨矿比表面积显著增大外,还在固体的表面和内部产生缺陷结构,增加了矿物表面的反应活性,改善了白钨矿的分解,使得白钨矿的浸出能在较低的温度顺利进行。     

THE EFFECT OF FURNACE ATMOSPHERE DUE TO COMBUSTION UPON HYDROGEN CONTENT IN LIQUID STEEL

<正> 在炼钢过程中,炉气中水汽是钢液中含氢的主要来源。就平炉而言,除了空气湿度和炼钢原材料带入炉中的水分以外,还有煤气燃烧生成的水汽。根据过去的研究结果,由于空气湿度直接或间接引起的水汽分压,一般波动于0.01—0.08个大气压之间,而煤气燃烧废气中的水汽分压则经常在0.1个大气压以上,有时甚至可以超过0.2     

氯化铜在水溶液中的扩散系数的测定SCIEI

用膈膜池法测定了298K条件下CuCl_2在CuCl_2和CuCl_2-HCl水溶液中的扩散系数。发现CuCl_2的扩散系数与其浓度依赖性主要取决于它的化学位和溶液的粘度。